请问如何检验钻石的真伪，以及他的纯度？？？

钻石鉴定与分级学

=================================

第4章 钻石加工

=================================

（一）引言

（二）钻石原石加工

（三）钻石首饰加工

第5章 钻石鉴定与分级

(一) 钻石鉴定

(二) 钻石分级

=================================

钻石的鉴定

=================================

5．1．1 放大镜检查

1、色散0044,有些仿制品如钛酸锶和合成金红石等的"火彩"远比钻石足,有些如YAG则远不如钻石

2、钻石为单折射,许多仿制品(如无色石英、黄玉、蓝宝石、锆石、合成金红石)呈双折射。可用放大镜来观察钻石腰棱是否有重影来判别是否呈双折射

3、可看透性(Read-through effect):将裸钻台面朝下,尖底朝上放置在有字的纸上,如是仿制品,一般明显可见纸上的字(低折射率),如是钻石,由于其高的折射率,一般从底部看不透纸上的字此法主要适用于按标准比例切磨的圆钻上,如钻石沾到液体,如水、酒精等,则钻石将具可看透性。

5．1．1 硬度检测

由于钻石具有最大的硬度,一般成品钻经多年佩带后仍有轮廓明显的小面棱,而大多数仿制品由于硬度比钻石低,易被磨损、磨圆、并留有划痕硬度检测通常不能解决问题,因为钻石不但有可能是存在天然的裂隙、解理,而且钻石尖部易刻划,甚至损伤另一颗钻石实属必须,则一般将钻石的腰棱在抛光的刚玉板上小心刻划,倘若它能划动刚玉板,则表明所检测的宝石即是钻石。

51．2 热导仪

这是目前鉴别钻石最有效、最普遍的工具,不论被检测对象大小或者是否切磨均可进行钻石热学性质在其鉴别中的另一个应用就是对一批相同大小的被测对象呵口气,钻石由于其极高的导热性,表面雾气消失极快

5．1．3 荧光检测

在长波紫外线辐照下,大多数钻石发出的是强弱不等的蓝-白色荧光钻石的这种效应崐在检测钻石群镶首饰时是非常有用的标志,因为不能指望许多钻石发出强度相同的荧光,若荧光强度不一,表明被测的宝石是钻石

5．1．4 光谱:见前述钻石的特性部分

5．1．5 X-射线

钻石具有低原子量,X-射线能轻易地穿透碳原子,换言之,钻石对于X-射线是透明的,而钻石的仿制品多是由大原子量的原子组成,如立方氧化锆原子量是钻石的6倍多,能吸收X-射线钻石的这一特性可用于它和其它仿制品的鉴别,方法是在一个有X-射线源的实验室内,将被测宝石放在摄影胶片上用X-射线照射,钻石会让X-射线透过并使胶片曝光,仿制品则吸收X-射线,其下的胶片未曝光冲洗胶片,检测未知宝石下面的胶片曝光度,即可知结果。

5．1．6 显微镜下观察

钻石具有特征的内部和表面特征,借助显微镜可将它和其他仿制品进行区分

(1)钻石由于极高的硬度,碾磨后刻面极为光滑,棱线锐利,一般仿制品则棱线较为圆钝, 甚至有不少碰伤缺口,刻面不如钻石刻面光滑

(2)真钻腰部可见毛发状的毛边,仿制品腰部范围内常见斜纹

(3)钻石在切磨过程中,为保留重量,常在腰部下方保留一些钻石原来的结晶面(原晶面),这些原晶面上往往会含有三角凹痕、平行槽痕等

(4)钻石内部常含角状包体(无色或有色的矿物晶体、石墨、深色硫化物包裹体等)仿制品则内部常含有圆形气泡

(5)标准切磨的钻石,小面排列几乎完全对称,仿制品由于成本低,常用机器自动切磨,小面排列常出现不对称的情况

(6)钻石的抛光痕迹不明显,其高硬度使得它只能在一定的晶格上抛光,不同刻面上的抛光痕迹的方向不同仿制品所有刻面上的抛光痕迹的方向不同仿制品所有刻面(至少在交棱处)的抛光痕迹通常是一个方向

(7)钻石常具内部透明纹,以适当角度照射时,一些细微而直的线或面贯穿钻石内部

(8)亭部闪烁检验: 用镊子或宝石夹将宝石亭部朝上放在显微镜光井上缘,在黑场照明下,前后轻轻摇动宝石观察来自亭部刻面的色散"闪烁"色钻石及主要仿制品的"闪烁"色分别是:

钻石: 大约相等的橙色、蓝色;

立方氧化锆: 主要是橙色闪烁;

钛酸锶: 呈多种光谱色;

YAG: 主要是蓝色和紫色;

GGG: 同钻石"闪烁"色

钻石与其仿制品的区别见(表1-1)

=======================================

5．2 钻石分级

=======================================

5．2．1 概述

任何一颗成品钻石的质量均可用以下四个标准来评价:

克拉重(Caratweight):钻石重量越大就越稀有因此,随着单颗钻石尺寸的增大,其价值也显著提高

成色(Colour):指钻石体色饱和度与理想无色状态的差异程度,越是无色的钻石越稀有

(花色钻石除外)

净度(Clarity):指钻石中的包裹体对其透明度的影响程度钻石净度越高越稀有

切工 (Cut): 切磨工艺使钻石显示瑰丽的程度

只有以上四个方面都得到评价,一颗钻石的质量和价格才能得到确定由于上述四个指标均以英文字母C开头,故钻石的评价又称4C评价评价的结果将详细记载在钻石鉴定书中

52．2 重量克拉

1、裸钻的克拉重量

如果成品钻石的所有其他因素(成色、净度、切工)均相同,则重量越大,价格也就越高在钻石业中,钻石的价格通常用"每克拉多少价"(PC)来表示钻石价格与克拉重的关系并不是简单的线性关系,而是一条在克拉溢价重量处出现台阶的线,如(图1-3)所示

图1-3 钻石价格与重量关系示意图溢价"台阶"还可出现在

025ct,05ct,075ct处

钻石的重量,既可用精密的电子或机械天平来测定(对未镶钻而言),也可用各种量规、钻石筛以及尺寸—重量计算法求得(主要用于已镶钻石的重量估算)

2、已镶嵌钻石

由于钻石一般的切割比率较有色宝石标准,故可用公式来计算其重量人造模仿品因比重较大,计算出的重量和实际的重量会相差较大,如差值大于20%则可怀疑是仿制品

计算公式:

圆钻: 重量=平均直径2×高度×00061

椭圆钻: 重量=平均直径2×高度×00062

心形钻: 重量=长×宽×高×00059 (长:宽)

祖母绿形: 重量=长×宽×高×00080 (100:100)

×00092 (150:100)

×00100 (200:100)

×00106 (250:100)

马眼形: 重量=长×宽×高×000565 (150:100)

×000580 (200:100)

×00585 (250:100)

×000595 (300:100)

梨形: 重量=长×宽×高×000615 (125:100)

×000600 (150:100)

×000590 (166:100)

×000575 (200:100)

52．3 成色

钻石有许多种颜色,最稀有的颜色是红色,然后依次为绿、蓝、紫和棕等颜色,这些有色的钻石往往被统称为异彩钻( Fancy Colour Diamonds ),因为它们在自然界非常稀少,故在价值上也较高氮的原子序数为7,与碳原子的大小很相近、故容易取代碳原子而存在于钻石中,大多数钻石的也因含有氮而多少带些**色调,这些微**的钻石就构成了所谓的**系列(Cape Series)钻石

最早的钻石成色分级是用南非钻石矿的名字来命名的,如Jager,River等,目前世界上主要的钻石分级体系是美国GIA和欧洲的CIBJO分级体系

表1-1 各种钻石成色等级比较对照表

━━━━━━┯━━━━━━━━━━━━┯━━━━━━┮━━━━━━━━━━━

美国宝石学院│ 国际珠宝联合会 │ 中国 │ 肉眼观察特征

(GIA) │ (CIBJO) │ │

——————┼————————————┼——————┼————————————

D │极白色(finest white) │ 100 │

——————┼————————————┼——————┤

E │极白(Finest white) │ 99 │

——————┼————————————┼——————┤一般肉眼观察无色

F │优白(Fine white) │ 98 │

——————┼————————————┼——————┤

G │ │ 97 │

——————┼————————————┼——————┤

H │白(White) │ 96 │

——————┼————————————┼——————┼————————————

I │淡白(Slightly white) │ 95 │小于02CT的钻石感觉不到

——————┤ ├——————┤颜色大颗粒钻石可感觉到

J │ │ 94 │有颜色存在

——————┼————————————┼——————┤

K │微白(Tinted white) │ 93 │

——————┤ ├——————┤

L │ │ 92 │

——————┼————————————┼——————┼————————————

M │一级黄(Tinted) │ 91 │

——————┤ ├——————┤

N │ │ 90 │ 一般肉眼感觉到具有

——————┽————————————┼——————┤颜色

O │二级黄(Tinted 2) │ 89 │

——————┤ ├——————┤

P │ │ 88 │

——————┤ ├——————┼————————————

Q │ │ 87 │ 一般人均感到**

——————┤ ├——————┼的存在,而且感到色调

R │ │ 86 │越来越明显

——————┼————————————┼——————┤

S-X │黄(Yellow) │ 85以下 │

━━━━━━┷━━━━━━━━━━━━┷━━━━━━┷━━━━━━━━━━━━

钻石的成色分级一般要求有以下四个基本条件,标准的灯源,标准比色石,良好的环境,以及受过训练的分级师成色分级一般采用比色法,即将待评价钻石与标准的比色样石进行比较,以决定待比未知样品的成色级别在与比色石比较时,应注意以下事项:

(1)保持要评价钻石的清洁;

(2)检查要评价钻石的特征,避免与比色石混淆;

(3)用冷光灯,背景要白色,不能有荧光;

(4)对比时,要注意对比两个相同的部位;

(5)对比时,要先后放在比色石的左、右二侧比较;

(6)比色时间勿太久,若一颗钻石的成色一时难以判定,应休息一会儿再比色

(7)比色只是一种相对的判断,故与比色者的心里状态有较大关系

(8)比色时还应注意钻石的成色与其大小、切割形状有关

52．4 净度

钻石的净度分级概念起源于20世纪初的巴黎,当时人们即按质量将钻石分为两种：

(1)"洁净"(Clean)钻石:无任何明显的内部瑕疵的钻石

(2)"不洁"(Pigue)钻石:具明显包裹体的较常见钻石

目前世界各地流行的钻石净度分级体系比上述两分法要详细得多(表1-3),分级时主要

依据钻石内部及外表的瑕疵,它们在国际上有统一的名称、标志及颜色

外部的瑕疵统一用绿色笔划,主要有:磨蚀(Abrasion)、多余刻面(Extra Facets)原晶

面(Natural)、伤痕(Nick)、小白点(Pit)、磨痕(Polish lines)、磨痕疤(Polish mark)等等。

内部的瑕疵特征统一用红色笔划表示,主要有: 毛边(Bearding、Feathering)、碎伤(Bruise)、破洞(Cavity)、缺口(Chip)、云状物(Cloud)、羽状裂纹(Feather)、结晶包体(Inhcluded Crystal)、内部生长线(Internal Graning)等等

表1-3 各种钻石净度等级系统对照表殔

━━━━━━━┯━━━━━━━┯━━━┯━━┯━━━┯━━━━━━━━━━━

美国 │国际钻石委员会│英 国│德国│中 国 │ 鉴定特征

———————┼———————┼———┼——┼———┼———————————

完全无瑕(FL) │ │ │ │ │10倍镜下干净

———————┤loupe clean │ FL │ IF │无瑕 ├———————————

内部无瑕(IF) │ │ │ │ │10倍镜下发现少量外部缺陷

———————┼———————┼———┼——┼———┼——————————

非常极微瑕VVS1│ VVS1 │ │ │ │10倍镜下可发现针状包裹体

———————┼———————┤ VVS │VVS │VVS │1-2个

非常极微瑕VVS2│ VVS2 │ │ │ │

———————┼———————┼———┼——┼———┼———————————

极微瑕VS1 │ VS1 │ │ │ │10倍镜下易发现少量细小

———————┼———————┤ VS │ VS │一号花│矿物包体

极微瑕VS2 │ VS2 │ │ │ │

———————┼———————┼———┼——┼———┼———————————

微瑕SL1 │ │ │ │ │10倍镜下十分容易发现矿物

———————┤ SL │ SL │ SL │二号花│包裹体,肉眼可见矿物包裹

微瑕SL2 │ │ │ │ │体

———————┼———————┼———┼——┼———┼————————————

一级瑕I1 │ P1 │1stPK │PK1 │三号花│

———————┼———————┼———┼——┼———┤肉眼可见矿物包裹体和大的

二级瑕I2 │ P2 │2ndPK │PK2 │四号花│解理及裂隙

———————┼———————┼———┼——┼———┤

三级瑕I3 │ P3 │3ndPK │PK3 │(大花)│

———————┼———————┼———┼——┼———┼————————————

│ │瑕明显│ │ 多 │

│ │瑕严重│ │ 瑕 │

│ │等外品│ │ 钻 │

━━━━━━━┷━━━━━━━┷━━━┷━━┷━━━┷━━━━━━━━━━━━

52．5 切工

钻石的切工,主要是指钻石切磨比例如何,抛光和后处理如何好的切工,是按标准比例切磨出的,在钻石内部,外部光线会从一瓣面折射至另一瓣面,然后从钻石的顶部散出,呈现出五颜六色的"光"如果不按标准比例切割,则切磨后的钻石由于不能将光反射出来,没有光,钻石就显得呆板,甚致出现黑底或鱼眼现象(详见加工部分)

标准的切工,共有57个面为了钻石的安全起见,一般50分以上的钻石,底部都要求有小面,因此共有58个面各小面的名称(见加工部分)

评价钻石切工好坏的方法既可用精密仪器,如台面量尺(Table Gauge)、钻石量尺(Micrometer)等,也可用目测法来进行大致的估计,后者往往更为便捷切工分级的主要评价指标有: 台面百分比、冠部角度、底部深度百分比、腰部厚度、尖底大小尺寸、修饰 (指抛光程度和对称程度)评估。

常见的关于的钻石术语，钻戒因为光芒璀璨又硬度较高，因此常被用来表示爱情，新人在结婚时也非常希望有一枚金光闪闪的钻戒，可是对钻石不够了解，购买钻戒时可能会受骗，下面就来看看常见的关于的钻石术语。

常见的关于的钻石术语：

1、AGTA

The　American　Gem　Trade　Association,美国珠宝协会。

2、AGSL

The　American　Gem　Society　Laboratories,美国权威的钻石检测机构。

3、Bar Setting 棒镶

钻石之间以金属分隔，并由左右的金属棒迫紧固定。

4、Brilliance 闪耀度

光线在钻石上全反射的白光强度。与切工比率以及对称性密切相关。

5、Characteristics 钻石的特征

钻石的天然生长痕迹和人为造成的缺陷。

6、Blemishes 表面瑕疵

包括表面花痕及色点, 抛光不当所致的糊状疤痕,表面很细的划伤的痕迹等。

7、Bearding须状裂痕

打磨过程中，可能出现的幼细裂痕。较轻微的裂痕经重新打磨，可被完全去除。

8、Bezel setting 包镶

这一镶嵌技术钻石完全地为形似画框的贵金属边缘所包围。

9、Baguette shape 长阶梯形

拥有阶梯切割面的长方形钻石。如较长的两边渐渐收窄，则称为尖阶梯形 tapered baguette。

10、Clarity grading 净度分级

每颗钻石都含有天然的内含物，犹如天然胎记，而这些内含物的数量、大小、形状、颜色则决定一颗钻石的净度及独特性。故名思义，内含物藏在钻石之内，而且可呈不同颜色：白、黑、无色、甚至绿色或红色。因此需在10倍放大镜下，对钻石内部和外部的特征进行等级划分。

11、Cavity 空洞

钻石大而深的不规则破口。

12、Colour grading 颜色分级

采用比色法，在规定的环境下对钻石颜色进行等级划分。

13、Bruises 击痕，擦伤

钻石受到外力撞击、摩擦留下的痕迹。

14、cut grading 切工分级

通过测量和观察，从比率和修饰度两个方面对钻石加工工艺完美性进行等级划分

15、Barion cut重子切割

Barion 切割拥有传统阶梯切割冠部及改良明亮式切割亭部，除亭尖外，方形Barion 切割的钻石共有62切面。

16、Carat 克拉

克拉这个词来源于一种叫作carob的植物种子，在古代人们用它来测量重量，一克拉等于200mg，142克拉等于一盎司，克拉可进一步划分为100分等于1克拉，半克拉的钻石也就是50分(大约100毫克)。

17、Channel setting 槽镶

常用于镶一排小的大小规则相同的宝石。这一镶嵌技术用两条金属从两边夹持宝石。用来镶圆形、狭长方形和方形宝石。槽镶就象一条铁轨，中间夹钻石。

18、Cleavage 破口

钻石腰部边缘破损的小口。

19、Crystal 内部纹理

钻石内部的天然结晶面。

20、Cloud 云状物

钻石中朦胧状、乳状、无清晰边界的天然包裹体。

21、Brilliant-cut 明亮式切割

经科学鉴定，明亮式切割反射最大部份光线，亦被誉为最闪烁及最具火采的切割方式。最普遍的明亮式切割圆形钻石具有58个切面，还有其它形状如心形、椭圆、榄尖形及梨形明亮式切割钻石。

22、Cluster setting 群镶

主石被较小的伴石包围，所以多颗较小的钻石，可组合成更大更漂亮的戒指。

23、Crown 冠部

腰以上部分，有33个刻面。

24、crown angle 冠部角

冠部主刻面与腰部水平面的夹角。

25、Culet 底尖(或底小面)

亭部主刻面的交汇点，呈点状或呈小八边形刻面。

26、crown proportion 宽高比

冠部高度相对于平均直径的百分比，计算公式见下

宽高比=冠部高度/平均直径×100%

27、culet proportion 底尖比(大小)

底尖直径相对于平均直径的百分比，计算公式见下

底尖比=底尖直径/平均直径×100%

By 2010 the most remarkable tide list

2010 absolute have every reason to believe this is a beautiful year - the financial crisis has become old news, garage, tight temporary accuse paragraphs of Shanghai world expo is in sight Into fashion version of this planet, Pandora will (the most compelling), Daedalian (clever, creative) and Delectable (pleasant) composed of "3D beauty" panoramic!

Keywords: high-tech

High-tech beauty into new trend

If you are still studying vitamin, spirulina etc natural ingredients, then you will "OUT" January 8,clarks womens smart, SEPHORA2010 spring media Open Day in 796 shanghart gallery was held From the overseas each big brand's founder, spokesperson, international trainer in succession to be present, transfer the brand's most sophisticated and off-the-press message In many new products, the most notable new trend is - the rise of high-tech beauty products Above all, the towers Sally card the launch of new light charm 525 skin bright, the palm type mining device of disc through wavelength 525 nano light, let users at home DIY complete high-tech whitening In addition, French high-tech beauty brand ESTHEDERM r&d "true cell water",Discount Tiffany Jewelry, EISENBERG to reaches ZhuoYan series using triple reactive molecules Have opened the cutting-edge technology of skincare fields

Keywords: drugstore

The pharmacy in cosmetics squad gradually strong

The so-called "drugstore",UGG, the most shallow understanding is that in pharmacy sell cosmetics and beauty da flamel will its summarized as four characters - - medical protect skin If again want detailed explanation, professionals said: "medical protect skin to taste in Europe is called drugstore,Herve Leger Bandage Dress, in Japan and the United States called drugs class cosmetics" In recent years,Dior Bangles, along with the people improve skin safety consciousness, more and more medicine makeup brand into pharmacy, drugstore market in China by YaYang, LiFuQuan and WeiZi occupied nearly 60 percent share at the same time, China's largest cosmetics company Shanghai home in has announced formally entered drugstore market

Shanghai home its drugstore brand jade ze listed at the same time, introduced first products jade zett embellish moisturizing milk According to information, this product is made up of brand and ruijin hospital in six years ago to establish the cooperation project of scientific research, mainly is for psoriasis, eczema, winter itching sickness and so on skin diseases In order to ensure product performance temperature close, jade zett embellish moisturizing milk is crocus oil added, such as supplementary affinity skin not saturated fatty acid, linolenic acid, linoleic acid and plant amide etc, can effective alternative water channel protein - 3 role In addition, it is absolutely not contain mineral oil, pigment and flavor, and after the ruijin hospital clinical efficacy verification, to improve the skin moisture content, reduce moisture loss, improve skin, relieve eczema,Timberland kids Boots, sensitivity dermatitis has remarkable auxiliary therapy effect

According to relevant market data display, 2004-2007, domestic drugstore market sales of annual growth rate are over 10-20%, 2008-2012, Chinese medicine market is expected to maintain makeup the growth rate However, China's current drugstore market annual growth is twice of the European market Besides according to reporter understanding, 2010 under shiseido pharmacy new brand also will enter the domestic pharmacy, come so, domestic drugstore squad has established Japan, France, the United States, and China's four big system, squad increasingly powerful

Keywords: new faces

SunFeiFei, under an international supermodel

Everyone knows "set" Karl gulag jezaniah the super star-generating ability,bose headpones, as long as he valued models in modeling not to GongDou difficult, before the end of last year ending the chanel "Paris - Shanghai" top hand gunsmith series 2009 year show, Chinese model SunFeiFei became the next a lucky dog -- because old Carl like her very much!

SunFeiFei 1989 was born in shandong weifang, early 2008 won the libs-elite Elite model contest champions, global China, which opened runners-up modeling career is in 2009 This long a east faces girl, different from cuckoo, PeiBei, her much a elegant beauty Surely, had the old Carl's commend, in 2010, international on beautiful field, the Chinese style breeze will again across T stage

Topics related articles：

mbt fuaba diamond

Air Jordan 11 Wear long skirt to cool enough

最近Tiffany 在上海办了一场迄今为止国内最大的高级珠宝展，其中最吸睛的一定是这颗重达 80 克拉的“帝国钻石”（The Empire Diamond），它的各项参数都是顶级——D 色、内部无瑕的品质，让人移不开眼！

这颗“帝国钻石”将会镶嵌在以1939年世博会典藏项链为灵感的作品之上，可能是Tiffany销售史上最贵的项链了！

无论是“帝国钻石”，或是“传奇黄钻”，不管是否能够拥有，钻石的魅力都让人无法抗拒。因为他们不仅光彩夺目，更重要的是它关联着我们对美的追寻，以及那些让人“无法呼吸的惊艳时光”。

就像戴在指尖的钻戒，不论何时何地，你都能感受到那份被珍视的美好 情感 。

其实选购钻石、定制钻戒都是需要花很多心思做功课的，相信大家一定很想知道这些！

1 钻石及其特性

钻石“Diamond”一词源自于希腊语“Adamas”，意为坚硬、不可驯服。它是世界上公认的最珍贵的宝石，也是最受人喜爱的宝石之一。

稀少、美丽、耐久的钻石成为了 四月生辰石和结婚60周年的纪念宝石 ，用坚不可摧的钻石来象征永恒的爱情，的确是一个浪漫而贴切的选择！

钻石的矿物名称是金刚石，在矿物学上属于金刚石族。其折射率为2417，是天然无色透明矿物中折射率最大的矿物，所以抛光良好的钻石具有很强的光泽和亮度。色散值为0044，也是所有天然无色透明宝石中色散值最高的矿物。

强“火彩”为钻石增添了无穷的魅力，同时也是我们肉眼鉴定钻石的重要依据之一。

2 钻石的分级标准

钻石4C分级想必大家都有所耳闻，指的是从克拉重量（Carat Weight）、颜色（Color）、净度（Clarity）、切工（Cut）四个方面，对钻石进行综合评价，进而确定钻石的价值。

钻石4C分级体系出现于20世纪50年代，由美国珠宝学院（Gemological lnstitute of America）总裁李迪克先生提出，是目前国际上最权威的钻石评价标准。

评价一颗钻石的依据就是证书，所以无论你在品牌专柜购买还是选择定制服务，只要认准GIA证书就可以啦！

克拉重量 Carat Weight

克拉（ct）是国际通用的的宝石质量单位，分（pt）则用于小于1ct钻石的计量。 1克拉=100分，50分=05克拉

这里补充讲一下，钻石这种珍贵宝石是存在克拉“溢价”现象的，钻石的级别越高，重量对价格的影响越大。也就是说如果你买相同品质、相同切割的90分和1克拉的钻石，看起来可能差不多，但价格会差挺多的。

两颗重量相等的钻石，由于净度、颜色、切工的不同，价值也有可能不同。重量无优劣，就看预算啦。

颜色 Color

20世纪50年代，GIA 对钻石的色级做了完整的划分，将颜色 从无色到浅** 分成了23个级别，分别用英文字母D Z表示，并有对应的钻石比色石标样与之对应。

钻石颜色等级参照图

一般选择H色及以上就可以~

净度 Clarity

钻石的净度是指其含有内含物和表面特征的程度。

那到底什么是钻石的内含物和表面特征？

钻石的内含物是指 包含或延伸钻石内部的天然包体、生长痕迹和人为造成的缺陷。 天然钻石在C元素受到高温和高压的影响形成的过程中，微小的晶体可能会包裹在钻石内部，晶体在生长过程中发生了原子结构异常，因此产生了钻石的内含物。

钻石常见的内部特征有：

1点状包体 pinpoint

2浅色包裹体 crystal inclusion

3深色包裹体 dark inclusion

4针状物 needle

5云状物 cloud

6羽状纹 feather

7内部纹理 internal graining

8内凹原始晶面 extended natural

9须状腰 beard

10空洞 cavity

11激光痕 laser mark

钻石的外部特征是指 暴露在钻石外表的天然生长痕迹和人为造成的缺陷。 除了少数几种之外，外部特征大多由人为因素造成，相对内部特征来说，外部特征对于钻石的净度影响较小。一些微小的外部特征经过重新加工去除，不影响钻石的净度等级。

钻石常见的外部特征有：

1原始晶面 natural facet

2表面纹理 surface graining

3抛光纹 polish lines

4刮痕 scratch

5烧痕 hurn mark

6额外刻面 extra facet

7棱线磨损 abrasion

8缺口 nick

9击痕 pit

10人工印记 inscription

GIA钻石净度标准分为6个大的类别和11个细分的等级， 净度等级越高，钻石的价格也就随之增高。

净度由高到低具体可分为：

FL,IF>VVS1,VVS2>VS1,VS2>SI1,SI2,SI3>I1,I2,I3

FL - Flawless，完美无瑕

在10倍放大镜下观察不到内含物和外部特征。

IF - Internally flawless，内部无瑕

在10倍放大镜下观察不到内含物，但可见轻微外部特征。

VVS1，VVS2 - Very Very Slight，含有少量微小的内含物

在10倍放大镜下极难发现（VVS1）到很难发现（VVS2），不允许有从台面中央可见的内含物。

VS1 and VS2 - Very Slight，含有少量微小的内含物

在10倍放大镜下观察困难发现（VS1）到较困难发现（VS2），允许有易见的外部特征。

SI1 and SI2 - Slight Inclusions，含有小内含物

在10倍放大镜下观察容易看到（SI1）到很容易看到（SI2）肉眼可能看见。

I1，I2 and I3 - Imperfect，内含物明显比较大，可以被肉眼看到。

切工cut

从原石到成品钻石，需要经过精细的切磨和复杂的工序，必须遵循光学定律，综合考虑亭深比、台宽比、冠高比，才能造就钻石的璀璨光芒。

GIA对D-Z颜色范围的圆形明亮式钻石的切工评定包括Excellent、Very Good、Good、Fair、Poor五个等级，越高级就越闪亮。

最好的切工，能够最好地展示出钻石的火彩和亮度。比如我们说的3EX切工，就是指切工、抛光、对称性三个指标都达到了excellent。

再来看看GIA证书中除了4C标准以外的重要参数含义：

- Fluorescence：荧光

荧光是指钻石在紫外灯照射下的发光特征。许多钻石在紫外光照射下产生荧光，荧光的颜色和强度也有所不同。荧光色通常是蓝白色，当光源内含有较多的紫外光时，受蓝白色荧光的影响，钻石的颜色会显得更白一些。

裸钻荧光按照GIA的分级标准分为N（无）- F（微弱）-M（中等）- S（强烈）- VS（非常强烈）。

- Inscription（s）：GIA腰码

每一张GIA证书都会有一个编码，为了让钻石能够对应GIA证书，防止套牌，会在钻石的腰部用镭射刻上证书编号， “GIA”字样为双线镂空， 只有用十倍及以上的放大镜才能看到。

除了腰码以外，GIA证书还会标注出钻石瑕疵的位置，也就是前面所说的钻石常见内含物和表面特征，用10倍放大镜看钻石是可以看到标注出的瑕疵的~

奶咖绿的问题也是经常困扰大家的，但是GIA证书上并没有标注其有无，那应该怎么看呢？

比如这样子

奶就是指带有奶油色调的钻石，因为钻石内部含有大量的针状体或者是云状物包裹体，会使钻石看起来如蒙上了一层雾。

咖就是指带褐色色调的钻石，绿就是指带绿色调的钻石。如果钻石带有咖、绿，钻石就不够透亮，影响观感。

3 钻戒的定制

选好钻石之后，就可以定制钻戒啦~这部分要准备的工作包括测量戒指圈号、挑选款式。

测量指圈

- 纸条(细绳)测量法

准备一张宽度小于1cm的长纸条，将纸条缠绕于指间两圈，一定要在手指关节最大处一圈，以舒适为宜，用笔在纸条重叠的位置做上记号，最后将纸条平铺，用刻度尺量出两点之间的距离，即为手指的指围。最好不要在天气过于炎热或者寒冷的时候测量~一般以傍晚时分为宜。

- 戒指内径测量法

之前有戴过戒指的，可以将内径垂直画在纸上，用刻度尺测量后对照尺寸表就可以啦。也可以把以前的戒指以前的戒指套在专业的戒指尺寸棒上边，记下刻度就可以。

挑选款式

钻石的款式主要看个人喜好，最经典的就是四爪、六爪，简约耐看~给大家列举一些大牌的款式

戒托的材质一般有18K金、铂（Pt950）。

18K金就是指金含量75%的合金；铂（Pt950）就是铂含量95%的合金。视觉上两种材质是接近的，但实际上各有所长。

相比铂金，18K金的硬度高，镶嵌比较牢固，不容易变形。~

而铂金化学性质稳定，不容易氧化变色，但由于硬度低，佩戴时间长了之后容易出现磨损现象。

4 钻石的保养

如何保持钻石的闪耀，就得在保养方面多下功夫了，这里给大家介绍几点精心保养钻石的tips：

- 远离油腻

钻石具有亲油性，容易将油渍、污渍沾染到表面，从而掩盖光泽，所以佩戴时应避免涂抹护手霜或使用肥皂，在洗碗和做家务的时候也应该摘下首饰，如果沾染油渍，可以用专业的首饰清洗液清洗。

- 避免接触强酸或强碱性的化学洗涤剂

此外，化妆品，漂白粉，各种清洁用化学用品，强酸强碱性化学洗涤剂会影响钻石的光泽，甚至使钻石出现斑点，影响钻石的美观。

- 避免剧烈撞击

钻石虽然坚硬，但是晶体特性具有完全解理，在特定角度撞击可能会破裂，因此要避免剧烈的敲击。

- 最好单独放置

需要避免与其他首饰混在一起放置，尤其应该与黄金首饰分离，因黄金较软，如果与坚硬的钻石首饰放在一起或佩戴在一起，很容易受损。

- 定期清洗

用一个小碗或者杯子装好温水，调好中性的清洁剂，将钻石浸在水中，用牙刷轻轻刷洗，再用一个网筛兜住，在水龙头下用温水冲洗干净，最后用柔软的绒布擦干即可。

前人早期研究资料显示，辽宁瓦房店地区钻石晶体普遍受到溶蚀，在晶面上形成有三角形和四边形凹坑，并有三棱台状、三角锥状、短柱状、参差状、波纹状、叠瓦状、鳞片状、圆盘状等的凸起，以及诸如蛀虫状、信封状、毛玻璃状和各种不规则的熔蚀坑、刻蚀沟、熔蚀空洞等。此外，在晶面上还常见有各种形状的晶纹，如蛛网状、塑性变形滑动线、面缝合线、束状晕线、圆饼状残余晶面等（赵秀英，1988;严春杰等，1989；郑建平，1989；宁广蓉，1999）。蚀象在大颗粒金刚石晶面上发育，而在小颗粒金刚石晶面上则不发育（图版Ⅲ），十二面体和立方体金刚石的蚀象较八面体金刚石蚀象要发育得多（赵秀英，1988;池际尚等，1996a；b），造成这种差异的原因池际尚等（1996a，b）虽进行过讨论，但成因未明。

本项目对搜集到的辽宁瓦房店地区292颗钻石样品的表面微形貌特征进行观测及统计。结果显示，钻石晶体普遍遭熔蚀，但熔蚀程度较浅，有相当比例的钻石晶面比较光洁，晶棱及角顶较为清晰尖锐。晶面花纹和蚀像种类按出现的频率由多至少的顺序主要有：溶蚀沟、闭合晕线、塑性变形滑移线、倒三角形凹坑、束状晕线、滴状丘、生长丘、叠瓦状蚀像、毛玻璃化蚀象等。

4211 生长丘

正三角形生长丘是在金刚石的（111）晶面上发育的与该晶面外形取向一致的三角形生长丘。其对称性与晶面的对称性完全一致，是晶体的生长形态 （图415，图416）。

图415 阶梯状、锯齿状生长纹

（6-LW，微分干涉显微镜，50×）

Figure 415 Stepped and jagged growth lines

（sample 6–LW，Differential Interference Contrast Microscope，50×）

图416 峰丛状的三角形生长丘

（样品LN-50-248，微分干涉显微镜，100×）

Figure 416 Peak-like triangular growth hillocks

（sample LN–50–248，Differential Interference Contrast Microscope，100×）

4212 熔蚀沟

钻石在生长熔蚀（解）的过程中，往往在其晶体上形成窄如裂缝的溶蚀沟，常沿解理面或与解理面重合的滑移面发展而成。在多数情况下溶蚀沟形成了复杂的弯弯曲曲的裂缝，不受任何一种确定的平面所限制。有时晶体上所生成的溶蚀沟不大，只“锯开”了顶角、边棱及部分晶面。但有时它们也会形成一系列交叉的深裂缝，把晶体割裂成形状不同的晶块，因此在晶体上便形成了碎块状的缺陷（图417，图418）。

金刚石形成过程中，若局部表面遭受熔蚀，则可能在晶体上发育熔蚀孔道和空洞。这些孔道和空洞如漏斗状或深坑状，在孔道的底部和壁上常见小的三角形和四边形花纹（图419，图420，图版Ⅲ）。

4213 滴状丘

滴状丘是金刚石晶面形成以后遭受熔蚀形成的表面微细形貌特征，多见于曲面晶体的曲晶面上，常见于沿塑性变形滑移线发育，彼此紧密排列成群分布（图421），或者是沿着位错露头溶蚀形成（图422）。

图417 晶体被熔蚀沟分割

（ LN-50-006，宝石显微镜，32×）

Figure 417 Crystal segmented by etched trench

（sample LN–50–006，Gem Microscope，32×）

图418 熔蚀沟

（LN-50-019，微分干涉显微镜，200×）

Figure 418 Etched trench

（sample LN–50–019，Differential Interference Contrast Microscope，200×）

图419 熔蚀空洞

（LN-50-015，微分干涉显微镜，200×）

Figure 419 Etched cavity

（sample LN–50–015，Differential Interference Contrast Microscope，200×）

图420 熔蚀空洞形成熔蚀孔道

（LN-50-253，宝石显微镜，50×）

Figure 420 Channel formed by etched cavity

（sample LN–50–253，Differential Interference Contrast Microscope，50×）

图421 滴状丘

（LN-50-253，微分干涉显微镜，100×）

Figure 421 Drop-like hillock

（sample LN–50–253，Differential Interference Contrast Microscope，100×）

图422 滴状丘

（12-LW，微分干涉显微镜，100×）

Figure 422 Drop-like hillock

（sample 12–LW，Differential Interference Contrast Microscope，100×）

4214 晕线

辽宁瓦房店金刚石中多边形闭合晕线是最为常见的晶体表面微细形貌特征之一。图423所示为一组围绕菱形十二面体角顶的闭合晕线，密集交错呈凸起状，晕线中心被一条长长的侵蚀裂隙穿过。图424为一组围绕角顶平行密集排列的闭合晕线。这种线状凸起是由于晶面分层熔解及生成熔解台阶而造成的微细层状蚀像。图425所示为一组较为平滑的束状晕线，具有磨蚀过的痕迹。

图423 闭合晕线

（LW-9，扫描电镜，55×）

Figure 423 Closed growth lines

（sample LW–9，Scanning Electron Microscope，55×）

图424 闭合晕线

（LW-12，扫描电镜，50×）

Figure 424 Closed growth lines

（sample LW–12，Scanning Electron Microscope，50×）

图425 束状晕线

（HN-120，扫描电镜，200×）

Figure 425 Bundle of lines

（sample HN–120，Scanning Electron Microscope，200×）

4215 塑性变形滑移线

塑性变形滑移线（图426，图427）是曲面晶体表面1～4组环绕晶体L5轴顶角的弧形复三方环，或1～4组垂直平行晶体L5轴晶棱的线状凸起（罗声宣等，1999）。它主要出现在金刚石{111}面上，有时为一组平行线，有时为两组相互交叉，有时可见三组交叉，很少在同一晶面上同时出现四组滑移线。滑移线的存在，表明晶体经历了强烈的应力作用，发生了塑性变形。当晶体受到很强烈的熔解时，就会因为受塑性变形带的影响，产生一组弯曲变形的滑动线（奥尔洛夫，1977）。塑性变形滑移线也是辽宁瓦房店金刚石样品中最常见的表面微形貌特征之一。

图426 平行的一组塑性变形滑移线

（LN-50-239，宝石显微镜，25×）

Figure 426 A group of parallel plastic deformation slip lines

（sample LN–50–006，Gem Microscope，25×）

图427 腐蚀后下凹的塑性变形滑移线

（LN-50-248，微分干涉显微镜，100×）

Figure 427 Plastic deformation lines sunk after erosion

（sample LN–50–248，Differential Interference Contrast Microscope，100×）

4216 倒三角形凹坑

倒三角凹坑是辽宁瓦房店金刚石最常见的表面微细形貌特征的一种。它形成于（111）面，与金刚石的晶面反向平行，三角形的角可以发生不同程度的钝化，形成六边形凹坑、四角或五角凹坑。根据倒三角凹坑的底部形态可将其分为两种类型：棱锥底三角凹坑和平底三角凹坑，棱锥底凹坑很浅，呈负三角锥状，它总是在晶格位错的露头处产生，平底三角凹坑与位错露头无关。当棱锥底三角凹坑进一步发育时，三角形蚀像加深并呈现出层状–阶梯状构造。在一些晶面上可以看到大小不等的倒三角凹坑，甚至有时候晶体的（111）晶面可以完全被倒三角凹坑覆盖。当比较小的三角凹坑叠加在比较大的三角凹坑之上时，可以区分出倒三角形蚀像的两个世代（图428，图429）。

图428 平底三角形凹坑群

（LN-50-232，宝石显微镜，40×）

Figure 428 Groups of flat base triangular etched pits

（sample LN–50–232，Gem Microscope，40×）

图429 平底三角形凹坑上布满细小三角形凹坑

（LN-50-232，微分干涉显微镜，200×）

Figure 429 A flat base triangular etched pit bestrewed with little triangular pits

（sample LN–50–232，Differential Interference Contrast Microscope，200×）

4217 叠瓦状蚀像

叠瓦状蚀象通常情况下发育在遭受强烈溶蚀的地方，是三角锥状丘和滴状丘的有规律组合。由于常见三角锥状丘和滴状丘沿滑移线发育，彼此紧密排列成群分布，所以叠瓦状蚀像的形状及分布特点可能取决于塑性变形，在塑性变形作用发生越强烈的地方，这种蚀象出现的可能性就越大，即取决于晶体平行{11l}面的滑移情况（图430）。

4218 四边形凹坑

四边形凹坑主要见于立方体面（100）方向，根据其底部形态可将其分为两种类型：棱锥底四边形凹坑和平地四边形凹坑。前者与位错的露头有关，后者与晶体结构有关（图431）。

4219 盘状蚀像

常见于浑圆晶体的曲晶面上。盘状蚀像是残留的原始平滑晶面部分，在蚀坑底部发育有清晰的沿一个方向排列的晕线。当浑圆晶体的大部分曲晶面都被强烈溶蚀时，只在个别部分残留有原始平滑晶面（图432，图433）。

42110 毛玻璃化蚀象

金刚石晶体的晶面因冲积磨蚀而产生的微细缺口可使其晶面变暗，具有油脂光泽，形成类似毛玻璃效果的表面形貌特征。但值得注意的是，提高放大倍数的时候，可以看见毛玻璃化蚀象实际上是十分微细的熔蚀现象，只是在低倍显微镜下不能进一步观察而已。样品LN-50-237为菱形十二面体金刚石，在低倍显微镜下可以见到其十二面体晶棱的交点处遭受熔蚀，呈现出毛玻璃化的效果，且可以见到楔形丘（图434）。当将毛玻璃化蚀象放大到500倍时，可见熔蚀面为微小的楔形丘，与晶体其他部位的楔形丘相对应（图435）。

与前人研究资料相比，本项目研究的292颗钻石的表面微形貌同样既有与生长过程有关的蚀像（生长丘），又有与熔蚀熔解有关的蚀像（熔蚀沟、倒三角形凹坑、晕线等），也有与塑性变形作用有关的线性结构（塑性变形滑移线），表明辽宁金刚石晶体表面微形貌种类相当丰富。在这些微形貌中，又以熔蚀沟、晕线、塑性变形滑移线、倒三角凹坑为主，表明辽宁金刚石晶体在形成过程中遭受了较强的熔蚀、塑性变形等地质作用。

图430 叠瓦状蚀像

（LN-50-104，微分干涉显微镜，100×）

Figure 430 Imbricated etched figures

（sample LN-50-104，Differential Interference Contrast Microscope，100×）

图431 平底四边形凹坑群

（LN-50-015，微分干涉显微镜，200×）

Figure 431 Groups of flat base quadrilateral etched pits

（sample LN-50-015，Differential Interference Contrast Microscope，200×）

图432 盘状蚀像、熔蚀沟

（LN-50-213，微分干涉显微镜，100×）

Figure 432 Etched disks，etched trench

（sample LN-50-213，Differential Interference Contrast Microscope，100×）

图433 盘状蚀像底部定向排列阶梯状结构

（LN-50-213，微分干涉显微镜，200×）

Figure 433 Bottom of etched disks oriented into a stepped structure

（sample LN-50-213，Differential Interference Contrast Microscope，200×）

图434 毛玻璃蚀象使晶体透明度降低

（LN-50-32，宝石显微镜，25×）

Figure 434 Crystal transparency decreased due to ground glass-like etched figures

（sample LN-50-32，Gem Microscope，25×）

图435 毛玻璃蚀象实为微小的楔形丘

（LN-50-33，微分干涉显微镜，500×）

Figure 435 Glass-like etched figures are in fact little wedge-like hillocks

（sample LN-50-33，Differential Interference Contrast Microscope，500×）